Iposii gilaasi gilaasi
Epoxy fiberglass tube ti wa ni ṣe nipasẹ okun didara gilasi ti o ga sinu epo-epo resini ti thermostability, eyiti o jẹ ohun elo ti o ga julọ bi ṣiṣe awọn ẹrọ ina foliteji giga, gẹgẹbi awọn fifọ, thimbles, awọn onigbọwọ ifowosowopo, awọn oniduro ohun elo afẹfẹ, ati bẹbẹ lọ.
| Iwọn inu inu (mm): | |||||
| Ø24 Ø30 Ø33 Ø36 Ø38 Ø42 Ø46 Ø48 Ø50 Ø52 Ø54 Ø55 | |||||
| Ø56 Ø58 Ø60 Ø63 Ø66 Ø74 Ø75 Ø76 Ø78 Ø Ø80 Ø82 Ø100 Ø105 | |||||
| Ø115 Ø130 Ø140 Ø144 Ø180 Ø1851 Ø94 Ø210 Ø240 Ø245 Ø250 Ø253 | |||||
Omiiran Inu ila opin wa.
Opin ti ita ati ipari le ṣee ṣe nipasẹ awọn ibeere pato awọn alabara.
Awọn ẹya ara ẹrọ
* Ti kii ṣe ibajẹ
* Iduroṣinṣin Dimensionally
* Iye Iye Ọmọ Iye Kekere
* Idinku Ina
* Rọrun lati Ṣiṣe ati Fi sii
* Itanna ti kii ṣe ifọnọhan
* Lightweight / Agbara giga
* Dena Bibajẹ Kokoro
* Agbara Ipa giga
* Gbigba Omi Kekere
* Agbara Flexural ti o tobi ju Igi lọ
* Ti kii-Leeching
Ti ara, ẹrọ ati ohun-ini aisi-itanna yẹ ki o tẹle tabili ni isalẹ:
| Imọ ibeere | |||||
| Deede Iwọn | Sisanra | Gigun gigun | Ifarada Ti gba laaye | ||
| inu iwọn ila opin | ita ila opin | Gigun gigun | |||
| 30 ~ 70 | 3 ~ 20 | 500 | ± 0,3 | ± 0,3 | 1 |
| 70 ~ 150 | 3 ~ 20 | 1000 | 0,5 | 0,5 | . 2 |
| 150 ~ 550 | 10 ~ 100 | 2800 | 0,5 | ± 0,2 | . 2 |
| Ti ara ati ẹrọ sile | Ti ara ati ẹrọ sile | ||||
| Orukọ Atọka | Kuro | Atọka | Orukọ Atọka | Kuro | Atọka |
| Iwuwo | g / cm3> | ≥1.80 | Iwuwo | g / cm3> | ≥1.80 |
| Gbigba omi | % | ≤0.15 | Gbigba omi | % | ≤0.15 |
| Iwuwo ti ìsépo (itọsọna yiyipo) | Mpa | ≥400 | Iwuwo ti ìsépo (itọsọna yiyipo) | Mpa | ≥400 |
| Iwuwo ti compress | Mpa | .98 | Iwuwo ti compress | Mpa | .98 |
| Agbara folti lori fẹlẹfẹlẹ afiwe ni ipo deede fun 5min | Kv | ≥25 | Agbara folti lori fẹlẹfẹlẹ afiwe ni ipo deede fun 5min | Kv | ≥25 |
| Layer folti ti inaro fẹlẹfẹlẹ ninu epo ni 90 ° C fun 5min | MV / m | ≥12 | Layer folti inaro fẹlẹfẹlẹ fẹlẹfẹlẹ ninu epo ni 90 ° Cfor 5min | MV / m | ≥12 |
Kọ ifiranṣẹ rẹ nibi ki o firanṣẹ si wa